Saturated solute transport micro-CT dataset in sintered glass and Bentheimer sandstone


Calibration experiments - 6 wt% CsCl Origin Data

8 repeat micro-CT scans of 12 s each (recon1 - recon8) were acquired when the sintered glass sample (6 mm diameter) was saturated with 6 wt% CsCl. The EMCT micro-CT scanner (designed and built in collaboration with TESCAN XRE, Belgium, www.xre.be) at UGCT (Ghent University, Belgium, www.ugct.ugent.be) was used with an accelerating voltage of 130 kV and a target power of 16 W. Every repeat scan consisted of 600 projections. The raw data was reconstructed to a 3D volume using Acquila (TESCAN-XRE, Belgium). The reconstructed voxelsize is 12.95 µm.

Segmented
No
Voxel length (x, y, z)
12.95, 12.95, 12.95 um
Sample
View Sample: Calibration experiments - sintered glass

Data

calibration_recon1_6percCsCl.raw
209.8 MB

Image Type 16-bit Unsigned
Width 538
Height 538
Number of Slices 380
Byte Order little-endian

calibration_recon2_6percCsCl.raw
209.8 MB

Image Type 16-bit Unsigned
Width 538
Height 538
Number of Slices 380
Byte Order little-endian

calibration_recon3_6percCsCl.raw
209.8 MB

Image Type 16-bit Unsigned
Width 538
Height 538
Number of Slices 380
Byte Order little-endian

calibration_recon4_6percCsCl.raw
209.8 MB

Image Type 16-bit Unsigned
Width 538
Height 538
Number of Slices 380
Byte Order little-endian

calibration_recon5_6percCsCl.raw
209.8 MB

Image Type 16-bit Unsigned
Width 538
Height 538
Number of Slices 380
Byte Order little-endian

calibration_recon6_6percCsCl.raw
209.8 MB

Image Type 16-bit Unsigned
Width 538
Height 538
Number of Slices 380
Byte Order little-endian

calibration_recon7_6percCsCl.raw
209.8 MB

Image Type 16-bit Unsigned
Width 538
Height 538
Number of Slices 380
Byte Order little-endian

calibration_recon8_6percCsCl.raw
209.8 MB

Image Type 16-bit Unsigned
Width 538
Height 538
Number of Slices 380
Byte Order little-endian